Duty temperature decides the construction before anything else does. At up to 80 °c, ptc immersion and liquid heaters is a candidate; the sections below set out what it will hold, what has to be true for it to hold it, and what fails first when it does not.
What the Up to 80 °C Band Requires
Comfort and condensation control: seat heating, mirror demisting, enclosure anti-condensation, battery pre-conditioning. Almost any construction reaches it, so the choice is decided by cost and thickness rather than by the temperature.
| Band | Up to 80 °C |
|---|---|
| This construction, continuous | 150 °C |
| Limited by | aluminium carrier with insulating film |
The band sits comfortably inside the 150 °C ceiling, which is where a heater should be specified: the margin between the working temperature and the insulation limit is what absorbs a poor thermal path, a warm ambient and a control overshoot without shortening the life of the part.
Why the Boundary Is Where It Is
80 °C is not a material boundary at all — every construction here passes through it — so the choice inside this band is decided by cost, thickness and area rather than by temperature. That is why printed film competes here and nowhere above it.
The engineering in this band is uniformity and control, not survival: comfort heating, condensation control and battery pre-conditioning all care about holding a few degrees evenly over a large area, which is a watt density and layout problem.
What a PTC Immersion and Liquid Heaters Is
Sealed PTC assemblies for warming water, coolant and washer fluid, where a dry-run cannot be allowed to destroy the heater.
Barium titanate ceramic whose resistance rises steeply above its Curie point, so the power it draws falls as the surface approaches that temperature. The element cannot exceed the Curie point it was made to, whatever the supply or the control does. In a sealed probe the Curie point is chosen below the boiling point of the fluid, so a dry tank stops the heater rather than destroying it.
The heat leaves through the wetted wall into the fluid. That path is excellent while the fluid is there and disappears entirely when it is not, which is why the dry-run case, not the running case, sets the design.
| Element | barium titanate PTC ceramic |
|---|---|
| Insulation system | aluminium carrier with insulating film |
| Total thickness | Element 1.5 mm to 3 mm; assembly to your drawing |
| Maximum size, one piece | M16 to M24 thread, 60 mm to 200 mm immersion |
| Continuous working temperature | 150 °C |
The continuous limit of 150 °C is set by aluminium carrier with insulating film. The element alloy would run far hotter; it is never the element that decides.
Which Temperature Is Being Held
Three temperatures matter and they are not the same number: the element temperature, the temperature of the surface being heated, and the ambient. A heater rated for a continuous working temperature is rated at the element — the hottest point in the assembly, and the one nothing on the outside is measuring.
The gap between element and surface is the thermal path. Bonded to metal it may be a few degrees; across an air gap, a void in the adhesive or a dry clamped joint it can be tens of degrees, and every one of them appears at the element rather than at the load.
Watt Density: the Two Figures
Two watt densities are quoted because there are two thermal situations. With nothing conducting heat away, 2 W/cm² is what the insulation survives. Bonded to a heat sink over the full outline, 10 W/cm² is. Anything in between depends on the quality of the joint, and the joint is the customer's to make.
The failure is silent and quick: the element does not know how it is mounted, so at 10 W/cm² in free air the heat simply accumulates in the insulation until it degrades. This is the single most common way these heaters are destroyed, and it happens on the first run rather than after a year.
A PTC assembly behaves differently at the limit. Deprived of its heat sink it does not run away; it reduces its own power. The consequence of a poor thermal path here is a heater that delivers well under its nameplate power, not one that destroys itself.
Control and Protection
This is the one construction here that limits its own temperature. Above the Curie point the ceramic's resistance rises steeply, the current falls, and the element settles rather than climbing — so a PTC heater cannot thermally run away even with the control shorted out.
That is a safety property, not an accuracy one. Self-regulation holds a surface somewhere near the Curie point under whatever cooling it happens to have; it does not hold a set point, and the temperature it settles at moves with airflow, with supply voltage and with the load. Where a number has to be held, a sensor and a controller are still required.
Two things still have to be designed for: the inrush, which is several times the running current while the ceramic is cold and which the supply and any switching device must tolerate, and the electrical fault case, which self-regulation does nothing about — a fuse or a current-limited supply is still the protection against a short.
Where This Construction Is the Wrong Answer
- Do not plan on running above 150 °C. That ceiling belongs to the insulation system, not to the element alloy, and it is not a figure that derating extends — past it the insulation degrades and the dielectric strength goes with it.
- Do not use self-regulation as a substitute for temperature control where a set point matters, and do not present it as a substitute for a fuse. It bounds the temperature; it does not hold a value and it does nothing about a short circuit.
Other Constructions That Hold Up to 80 °C
Constructions in this catalogue that will hold up to 80 °c continuously:
How to Specify One
This is a made-to-drawing part, so there is no catalogue number to quote. A quotation is built from the following, and the more of it that arrives with the enquiry the fewer rounds it takes:
- An outline drawing, or a sketch with dimensions: overall size, holes, cut-outs, radii and the lead exit position.
- The supply voltage, and whether it is AC or DC. The element is wound for one voltage; it is not a switchable range.
- The power required, or — better — the temperature to be reached and the mass or flow it has to be reached in. Given the second, the wattage can be calculated instead of guessed.
- What the heater is attached to, and how. This is what decides which watt density figure applies, and it is the question a quotation cannot proceed without.
- The ambient, and the lowest temperature the assembly must start from. A heater sized for a 20 °C start is undersized for a -30 °C one.
- Duty cycle: continuous, intermittent, or a warm-up to a deadline. Time to temperature is a specification, not a by-product.
- Sensor and protection: which sensor, where it goes, and which limit device is fitted in series with the element.
- The certification the end product is built to, named on the enquiry rather than after approval.
- Quantity and target price, because the construction that is right for fifty pieces is often not the one that is right for fifty thousand.
- The Curie point wanted, and the airflow or thermal path the assembly will have — both decide the power the element will actually deliver.
Lead time: Samples 7-10 days from approved drawing; production 15-20 days.
PTC Immersion and Liquid Heaters — Capability Table
These are process limits for the construction, not the specification of one stocked item. Every line is what the factory can hold; what your part holds is fixed on your drawing.
| Parameter | Specification | Limit / note |
|---|---|---|
| Construction | Barium titanate PTC ceramic, electroded on both faces, in an aluminium carrier | Assembly built around the element to suit the load |
| Curie temperature | +80 u00b0C to +150 u00b0C, selected | Selected at order u2014 it is the surface temperature ceiling and cannot be adjusted afterwards |
| Self-regulation | Power falls to a fraction of rated as the surface reaches the Curie point | No thermostat is required to prevent runaway; one may still be wanted for control |
| Element size | M16 to M24 thread, 60 mm to 200 mm immersion | Standard element footprints; assemblies to your drawing |
| Supply voltage | 12 V, 24 V, 110 V, 220 V | The same element works over a voltage band with different output |
| Power output | 2.0 W/cmu00b2 typical in still air, 10.0 W/cmu00b2 with forced air | Output is set by the airflow, not by a setting u2014 this is what self-regulating means |
| Inrush current | 3 to 8 times running current for 1 to 3 seconds | The supply and any relay or MOSFET must tolerate it |
| Dielectric strength | 1800 V AC, 1 minute, element to case | On the assembled unit with its insulation in place |
| Insulation resistance | greater than 100 Mu03a9 at 500 V DC | |
| Terminations | Faston 2.8/4.8 mm, crimp, or flying leads | Chosen for the assembly temperature |
| Life | Over 10,000 hours at rated conditions | Ageing shows as a slow rise in cold resistance, not as sudden failure |
| Certifications available | UL 499, IEC/EN 60335, RoHS, REACH, CE, IATF 16949 | Construction level |
| Dry running | Survives it: output collapses as the surface reaches the Curie point | The single strongest argument for PTC in a liquid application |
| Sealing | O-ring or bonded seal, IP67 at the terminal end | Fluid compatibility is checked at quotation u2014 coolant additives attack some elastomers |
Capability figures are for barium titanate PTC ceramic elements and the aluminium assemblies built around them. The defining property — that power falls steeply as the element approaches its Curie point, so surface temperature cannot run away — is inherent to the ceramic, not a feature of the control.