Insulation system page for pet film heaters with psa backing built in PET Polyester Film. The ceiling (-40 °C to +120 °C continuous), the mechanical behaviour, the dielectric strength, the failure route out of the material, and the constructions to move to when the duty goes past it.
PET Polyester Film as an Insulation System
The low-cost thin-film substrate, printed rather than etched. Roll-to-roll production makes it the cheapest heater per square metre by a wide margin at volume.
| Working range | -40 °C to +120 °C continuous |
|---|---|
| Total thickness in this construction | 0.3 mm |
| Dielectric withstand | 1500 V AC, 1 minute |
| Insulation resistance | greater than 100 Mu03a9 |
| Maximum size, one piece | 400 x 800 mm |
A flexible insulation has to do three jobs at once: hold off the supply voltage, survive the element temperature, and bend without cracking. Thickness trades against all three — a thinner build responds faster and conforms better, and has less material between the element and whatever the heater is touching.
The Temperature Ceiling, and What Sets It
Working range: -40 °C to +120 °C continuous. The ceiling belongs to the insulation. Nichrome will run red; pet polyester film will not, and it is the material around the element that decides what the part is rated at.
This construction is rated 120 °C continuous. That is a continuous figure at the element, not an ambient and not a surface temperature measured somewhere convenient — and it is not a figure that derating extends downwards from something higher. Past the ceiling the insulation degrades, the dielectric strength falls with it, and the failure is electrical rather than thermal.
The boundaries across this catalogue are all material boundaries: PET stops at 120 °C, filled epoxy at 150 °C, silicone rubber and polyimide at 200 °C, and above that only fired and inorganic systems — thick film on stainless or alumina, and mica — are candidates at all.
What Attacks PET Polyester Film
PET softens above about 130 °C and loses its dielectric strength there. It is not a candidate for anything that can dry out and overshoot.
What a PET Film Heaters with PSA Backing Is
Standard printed film heaters supplied with adhesive and a liner, for bonding to plastic, glass or sheet metal in assembly.
Carbon or silver ink screen printed onto PET polyester film, laminated and die cut. It is made on a roll, which makes it the cheapest heater per square metre by a wide margin at volume, and it stops at 120 °C because the film does.
The heat leaves through the bonded face. Everything that is not in contact with the load radiates and convects from the back of the heater instead, which at these thicknesses is a poor path — so an air gap under part of the outline is not a small loss of efficiency, it is a hot spot at that spot.
| Element | screen-printed carbon or silver ink |
|---|---|
| Insulation system | PET polyester film |
| Total thickness | 0.3 mm |
| Maximum size, one piece | 400 x 800 mm |
| Continuous working temperature | 120 °C |
The continuous limit of 120 °C is set by PET polyester film. The element alloy would run far hotter; it is never the element that decides.
Above Its Ceiling: What to Use Instead
Above 120 °C the film softens and its dielectric strength goes with it, so the answer is a different construction rather than a derated one: polyimide to 200 °C at a similar thickness and a much higher watt density, silicone rubber to 200 °C where the surface is curved or the part needs to be tough, and thick film where the duty is above 200 °C. Below 120 °C nothing beats PET on cost per square metre at volume, which is the whole reason it exists here.
What the Insulation Changes About the Heater
The insulation decides the thickness (0.3 mm here), and the thickness decides the response: less material between the element and the load means less to heat before anything useful happens, and less thermal resistance in the way of the heat that follows. It also decides what the heater will wrap around — this construction wraps a cylinder but will not take a compound curve.
Watt Density: the Two Figures
Watt density, not wattage, is what the construction is limited by. 0.1 W/cm² unbonded and 0.5 W/cm² bonded to metal are the limits for this build — so if the wattage is fixed by the duty, the area is what has to move.
Where the required power will not fit into the available area at the free-air figure, the answer is a better thermal path rather than a thinner margin: bond the whole face down, or add a spreader plate. On 150 cm² the difference is roughly 15 W against 75 W, which is usually the whole argument.
Control and Protection
This heater has no way of limiting its own temperature. Resistance heating draws roughly the same power whatever the temperature, so with the load removed, the fluid gone, the fan stopped or the sensor open circuit, the element keeps producing watts until something stops it.
The design must therefore contain a control device and, separately, a protective one: a controller with a sensor to hold the set point, and a bimetal thermostat or a one-shot thermal cutoff wired in series with the element to open the circuit if the loop ever fails. The two are not interchangeable — a controller that has lost its sensor cannot protect anything, which is exactly the fault the cutoff exists for.
PET softens at about 130 °C and loses its dielectric strength as it does, so the cutoff temperature has to sit under that with margin. This is a construction that cannot be allowed to dry out and overshoot.
Sensors can be built into the part: NTC thermistor, PT100 or PT1000 RTD, or a K-type thermocouple, fitted under the same insulation and tested with the heater as one assembly. A sensor laminated into the heater reads the heater; a sensor on the load reads the load. Both are legitimate, and the drawing has to say which is wanted.
T
h
How This Construction Fails
- Run at the bonded watt density in free air. The insulation reaches its limit within minutes and the element burns through where the local density is highest. Specify at 0.5 W/cm² only where the heater is genuinely bonded to metal over its whole area; unbonded, the figure is 0.1 W/cm².
- Voids under the bond. Air trapped during application, a contaminated surface or an adhesive that never reached full cure all produce the same result: a patch with no thermal path, running far above the rest of the heater, which is where the failure starts.
- Loss of the control loop. An open-circuit sensor, a welded relay contact or a controller in manual leaves the element at full power with nothing watching it — the case the series thermal cutoff exists for, and the reason it must not be omitted to save a part.
- Overshoot into the film. PET softens from about 130 °C and its dielectric strength goes with it, so a fault that a silicone heater shrugs off destroys a PET element.
- Silver migration. A printed silver circuit under a DC bias, in humidity, grows dendrites between adjacent tracks; carbon does not, which is one reason carbon is still used where the geometry allows it.
Leads and Terminations
Lead wire as supplied: Crimped or soldered leads, or a printed silver bus bar with a bonded tail. Length, gauge, exit position and termination are drawing items — the exit position in particular, because it decides where the heater can be routed and it cannot be changed after the tool is cut.
The lead exit is a thermal discontinuity as well as an electrical one. The joint between a fine element and a stranded lead is the hottest point of many heaters, so it is kept out of the highest watt density zone, strain relieved, and — where the exit sits in a hot area — insulated in PTFE rather than in silicone.
How to Specify One
This is a made-to-drawing part, so there is no catalogue number to quote. A quotation is built from the following, and the more of it that arrives with the enquiry the fewer rounds it takes:
- An outline drawing, or a sketch with dimensions: overall size, holes, cut-outs, radii and the lead exit position.
- The supply voltage, and whether it is AC or DC. The element is wound for one voltage; it is not a switchable range.
- The power required, or — better — the temperature to be reached and the mass or flow it has to be reached in. Given the second, the wattage can be calculated instead of guessed.
- What the heater is attached to, and how. This is what decides which watt density figure applies, and it is the question a quotation cannot proceed without.
- The ambient, and the lowest temperature the assembly must start from. A heater sized for a 20 °C start is undersized for a -30 °C one.
- Duty cycle: continuous, intermittent, or a warm-up to a deadline. Time to temperature is a specification, not a by-product.
- Sensor and protection: which sensor, where it goes, and which limit device is fitted in series with the element.
- The certification the end product is built to, named on the enquiry rather than after approval.
- Quantity and target price, because the construction that is right for fifty pieces is often not the one that is right for fifty thousand.
- Whether adhesive backing is wanted, and what surface it goes onto — a low-energy plastic needs a different adhesive from bare aluminium.
Lead time: Samples 7-10 days from approved drawing; production 15-20 days.
PET Film Heaters with PSA Backing — Capability Table
These are process limits for the construction, not the specification of one stocked item. Every line is what the factory can hold; what your part holds is fixed on your drawing.
| Parameter | Specification | Limit / note |
|---|---|---|
| Construction | Carbon or silver ink on PET with 3M PSA backing | Decided at quotation from the outline and the wattage |
| Insulation system | PET polyester film, 0.05 mm to 0.125 mm per face | This is what sets the temperature limit, not the element |
| Total thickness | 0.3 mm | Nominal, before adhesive; add 0.2 mm for PSA backing |
| Minimum size | 20 x 20 mm | Below this the element cannot be routed with a safe edge margin |
| Maximum size, one piece | 400 x 800 mm | Larger areas are supplied as tiled zones with separate circuits |
| Dimensional tolerance | u00b11 mm on the die-cut outline | On the die-cut outline; hole positions are held tighter |
| Supply voltage | 12 V, 24 V, 48 V, 110 V, 220 V | Wound to the ordered voltage u2014 it is not a switchable range |
| Resistance tolerance | u00b110% standard, u00b15% on request | Measured at 20 u00b0C; hot resistance differs with the element alloy |
| Watt density, free air | 0.1 W/cmu00b2 typical | Nothing conducting heat away u2014 the honest figure for an unbonded heater |
| Watt density, bonded to heat sink | 0.5 W/cmu00b2 maximum | Only valid with full-area contact to metal; specifying at this figure and running in free air destroys the heater |
| Continuous working temperature | -40 u00b0C to +120 u00b0C continuous | Of the heater itself, measured at the element, not the ambient |
| Dielectric strength | 1500 V AC, 1 minute | One minute, element to any exposed surface, no breakdown |
| Insulation resistance | greater than 100 Mu03a9 | At 500 V DC, measured after the dielectric test |
| Lead wire | Crimped or soldered leads, or a printed silver bus bar with a bonded tail | Length, gauge and termination to your drawing |
| Attachment | PSA backing standard; laminated into the end product at high volume | Adhesive-backed heaters need continuous contact pressure while curing |
| Sensor and control options | NTC 10K B3950 bonded to the film, or a printed PTC ink track | Fitted under the same insulation and tested as one assembly |
| Certifications available | IEC/EN 60335, UL 94 V-0, RoHS, REACH, CE, IATF 16949 | Constructions are built to these; the certificate covers the construction, not every outline |
Capability figures are for screen-printed carbon or silver ink on PET polyester film. The +120 °C continuous limit is the film's, and it is a hard limit: PET softens and loses dielectric strength above roughly 130 °C, so this construction is only a candidate where the maximum credible temperature is bounded well below it.